PA-CF (Carbon Fiber Reinforced Nylon)
Performance Rating
Compare All Filaments →Rated on 5 criteria: print temperature, warping, strength, creep resistance, and heat resistance (★1-5).
Print Temp
Nozzle: 250-280°C
Bed: 80-100°C
Warping
Rated
Strength
Bending Strength: (74.50 MPa)
Creep Resistance
Rated
Heat Resistance
Heat Resistance Temp: 105°C
Features
- Carbon fiber reinforced PA. High strength and wear resistance.
- Industrial high-performance parts
- Excellent dimensional stability
Basic Information
Classification:Advanced
Base Resin:Polyamide + Carbon Fiber
Melting Point:220-240°C
Density:1.10-1.15 g/cm³
Shrinkage Rate:0.5-0.8%
Heat Resistance:100-110°C
Recommended Settings
| Item | Recommended Value | Notes |
|---|---|---|
| Nozzle Temperature | 250-270°C | Higher than standard PA |
| Bed Temperature | 80-100°C | Prevent warping |
| Fan Setting | 0-30% | Prioritize layer adhesion |
| Print Speed | 30-50mm/s | Quality focused |
| Nozzle Diameter | 0.4mm or larger | Hardened steel required |
| Caution | Drying required (80°C, 4+ hours) | |
Bending Strength
| Item | Measured Value |
|---|---|
| Default (Flat Layout) | |
| Bending Strength | 74.5 MPa |
| Flexural Modulus | N/A |
| Test Method | 3-Point Bending Test（Details） |
Stress–Strain Curve
Bending test data for this filament has not been registered yet.
The graph will be displayed once data is added.
Use Cases
Suitable Applications
- • High-performance gears
- • Industrial jigs
- • Mechanical parts
- • Structural parts
Pros & Cons
Pros: High strength, wear resistance, dimensional stability
Cons: Nozzle wear, hygroscopic, drying required, very expensive
Precautions
• Hardened nozzle required.
• Drying before use is required.
• Enclosed chamber printing recommended.